SM2R-GNK.SAARSTAHL
MAG-wire electrode / TIG welding rod
Type: Drawn copper-plated
Area of application/characteristics:
For MAG or TIG fusion welding of materials same and similar in type; deposit welding of age-hardenable deposits.
SM2R-GNK.SAARSTAHL
MAG-焊丝/ TIG 焊丝
类型：拉拔镀铜
应用领域/特性：
用于MAG或TIG熔焊或堆焊时效硬化沉积及相同或相似材料。
Standard identification | |
Material No. | ≈1.6356 |
| 标准规格 | |
钢号 | 近似1.6356 |
Chemical composition (standard values/wire analysis in %) | |||||||
C | Si | Mn | Cr | Mo | Ni | Co | Ti |
0.010 | 0.40 | 0.10 | 0.20 | 4.00 | 18.0 | 12.0 | 1.60 |
化学成分（标准值/焊丝分析%） | |||||||
C | Si | Mn | Cr | Mo | Ni | Co | Ti |
0.010 | 0.40 | 0.10 | 0.20 | 4.00 | 18.0 | 12.0 | 1.60 |
not exceeding *不超过
The chemical composition of the pure weld deposit depends on the weld parameters applied.
焊接沉积的化学成分纯粹取决于焊接工艺参数的应用。
Mechanical properties(weld deposit , untreated) | ||||
Welding process | Rm(N/m㎡) | Rpo,2(N/m㎡) | A5(%) | Av at RT ISO-V(J) |
MAG/TIG | All values approx. as for basic steel mat. no. 1.6356 | |||
机械性能（未热处理的焊区） | ||||
焊接方法 | 抗拉强度 | 屈服强度 | 断面收缩率 | 冲击功 |
MAG/TIG | 所有的标准值都接近1.6356 | |||
Welding parameter(shielding gases acc. to DIN EN ISO 14175 : 2008-06) | |||
Type of process | Shielding gas | Type of process | Shielding gas |
MAG | M12/M13 | TIG | I 1/pure argon |
焊接工艺（保护气体根据DIN EN ISO 14175:2008-06） | |||
焊接形式 | 保护气体 | 焊接形式 | 保护气体 |
MAG | M21 | TIG | 纯氩气 |
Type of current | Weld positions | |
MAG-wire electrode | Direct current(+ pole) | PA PB PF PC PD PE PG |
TIG-welding rod | Direct current(-pole) | PA PB PF PC PD PE |
电流形式 | 焊接位置 | |
MAG-焊丝 | 直流电（+极） | PA PB PF PC PD PE PG |
TIG-焊丝 | 直流电（-极） | PA PB PF PC PD PE |
Dimensions(mm) | ||||||||
MAG-wire electrode | 1.00 | 1.20 | 1.60 | |||||
TIG/1=1,000mm | 1.00 | 1.20 | 1.60 | 2.00 | 2.40 | 3.00 | 3.20 | 4.00 |
尺寸（mm） | ||||||||
MAG-焊丝 | 1.00 | 1.20 | 1.60 | |||||
TIG/1米长焊丝 | 1.00 | 1.20 | 1.60 | 2.00 | 2.40 | 3.20 | 3.20 | 4.00 |